product overview
The high temperature lithium compound grease is made by thickening refined mineral oil with avariety of composite metal soaps at high temperature and high pressure, and adding high efficiencextreme pressure anti-wear agent, anti-rust antioxidant, etc., which is a long-term high temperatureresistant and long life grease.
performance characteristic
Good extreme pressure anti-wear performance, to meet the lubrication of heavy duty automobile hub bearings.
Good high temperature performance, high temperature adhesion, can ensure good lubricating oil film.
Good colloidal stability, long service life of grease, can extend the grease change cycle.OGood water resistance and protection.
Recommended application
lt is suitable for lubrication of wheel bearings, chassis, motor pumps and other friction parts ottrucks, construction machinery vehicles, large buses and heavy-duty trucks under harshconditions such as medium speed and heavy load.
Operating temperature:-30°C ~220°C
Typical data
| Item |
Typical data |
Test nethod | ||
|
NLGI 1 |
NLGI 2 | NLGI 3 | ||
|
Appearance |
Smoothing cream |
visual | ||
|
Worked cone penetration，0.1mm |
315 | 270 | 228 | GB/T 269 |
|
dropping point，℃ |
274 | 280 | 285 | GB/T 3498 |
|
penetration change after 100,000 strokes，0.1mm |
17 | 20 | 23 | GB/T 269 |
|
carrying capacity (four ball method)PB value,N |
617 | 617 | 617 | SH/T 0202 |
|
carrying capacity (four ball method) PD value,N |
3089 | 3089 | 3089 | SH/T 0202 |
|
carrying capacity (Timken method) OK value, N |
156 | 156 | 156 | SH/T 0203 |
|
Anti-corrosion property(52℃,48h) |
Up to standard | GB/T 5018 | ||
|
Steel mesh oil separation（100℃，24H）% |
1.0 | 0.5 | 0.4 | SH/T 0324 |
|
Similar viscosity(-10°C,10s-1),Pa·s |
607 | 810 | 1200 | SH/T 0048 |